| Abrasion Resistance |
97.4% Greater
than Concrete ASTM C-944 |
| Applied Thickness |
2 Inches Minimum |
| Coefficient of
Thermal Expansion |
11-12x10(-6th
power) Units Per Degree F. |
| Compressive Strength |
To 15,000 p.s.i.
ASTM C 579-75 |
| Curing Time |
15 to 60 minutes |
| Density |
150 lbs./cu.
ft. |
| Electrical Conductivity |
3.31 x 10(-8
power) ohm/cm(-1 power) ACI Monograph No. 6, ASTM D-257 |
| Flexural Strength |
To 3,000 p.s.i.
ASTM C 580-74 |
| Freeze Thaw Strength |
After 300 Cycles
- No Loss, No Cracks ASTM C-666 |
| Heat Resistance |
400 Degrees F.
/ 24 hrs. 100% Strength Retained |
| Modulus of Elasticity |
4.0x10(6th power)
p.s.i ASTM C-469 |
| Operating Temeratures |
To 250 F in most
Media |
| Porosity |
0.1% to 0.30% |
|
Priority Pollutants Extraction Acids,
Bases, Metals and Synthetic Organic Pesticides
|
Below Detection Limits,
ppm E.P. Tox and S.O.C.
|
| Shrinkage |
Less Than .1% |
| Tensile Strength |
to 2,000 p.s.i.
ASTM C 307-77 |